Sommarju tal-EPS(Polistirene espansibbli) Produzzjoni ta 'materja prima

Introduzzjoni tal-fluss tal-proċess

The process of one-step method including polymerization, impregantion, cooling, washing, drying, sieving, coating, vibration examation, packing. The average production cycle time of the EPS production is 16~17 hours.

(1) Polimerizzazzjoni u impregnazzjoni

Polymerization and impregnation is proessed in the reactor. Under certain temperation, SM will polymerize. By comtinuous stiring, SM will be extended and cut into strips, then composing SM oil drops suspending in the water because of the surface pressure. There are dispersants suspending in the water to avoid SM particles bump and connect together. In this process the diserse power should be larger than the connect power to ensure the low-temperature polyerization.

The low-temperation polymerization reaction is running in the oil drop of SM, the heat released in the reaction will be taken away by the cooling water in the clip set. To remove the heat in time, we must ensure the normally work of recycling water system during reaction process. Otherwise, the temperature in the reactor will be too high, which lead to quick reaction and higher viscosity.

The beads production process is controlled manually, during the process, the temperature should be controlled proper to avoid large fluctuation, otherwise, the size range of beads will be widened. Meantime, frequently observation of samples is essential to control the size of beads.

Bl-aġġustament ta 'piż ħafif CaCO3 u TCP, id-daqs ta' żibeġ jista 'jiġi kkontrollat.

DCS system is used for temperature control during the whole process of heating, polymerization, impregnation, high-temperature reaction, and cooling. To ensure safety production, the DCS system will control the reaction temperture and time, and alarm in over-temperature or overpressure case.

When the conversion rate of SM reach approximately 75%(about 4 to 5 hours under constant temperature), certain quantity of blowing agent should be added. After the impregnating and polymerization under certain time and pressure, we can get EPS beads.
The blowing agent for impregnation is injected into measuring kettle by pump, and accurately weighted by weighting device. After the high-tempterature process, when cooling to the specified temperature, the material can be discharged to washing tank.

(2) Ħasil

The impurities such as dispersant and defloculates must be removed by washing. After cleaning, the EPS beads will be dried by centrifugal dehydration to remove most surface water, and ready for further drying.
Nistgħu wkoll nużaw aġent de - foaming biex ineħħu l-impuritajiet.

(3) tnixxif

After centrifugal dehydration, there would be about 3% water residue on the surface of EPS beads(highly water content will influence the quality of EPS products), so further drying process is needed, during this process, EPS beads are dried by hot air. Blowing by hot wind, the surface resident water become steam, then this kind of gas-solid mixture come into the diffusion type cyclone separator, while the beads fall to filter silo through outlet, the high-speed revolving airflow will form a low pressure area in the center of the separator, and push the hot humid air flow up through the center pipe. In this way the beads will be dried.

After hot air drying , the beads need to be cooled by cold wind to further reduce the water content, and get ready for the screening. To prevent the accumulation of electricity, antistatic agent should be added during drying.
It-temperatura tat-tnixxif hija kkontrollata mis-sistema DCS.

(4) Screening

Id-daqsijiet ta 'żibeġ imnixxfin tal-EPS huma irregolari, hemm bżonn ta' skrining biex tissepara ż-żibeġ billi tispeċifika u tittrasferixxi għal silos differenti.

(5) Kisi

During the EPS production, storage, transportation and process, the escaping of blowing agent is inevitable. If too much blowing agent lost, many problems will occurred, such as decrease of expanding rate, increase of density, difficulty of forming, etc. To extend the valid storage period of EPS, and prevent the loss of blowing agent, the use of coating agent at the surface of EPS is essential.

(6) Pakkett

Ippakkja ż-żibeġ tal-EPS skont l-ispeċifikazzjoni differenti. Il-piż standard tal-pakkett huwa 25kg.

Għan tal-imballaġġ: trasport tal-konenjenza, evita l-ħarba tal-aġent li jonfoħ, u testendi l-perjodu ta 'garanzija.

Ċart tal-fluss tal-EPS

Każ